CARBON TELESCOPIC SYSTEMS

provide maximum control and stability when extended for a variety of applications (window cleaning equipment, marine life systems, etc.). When inserted, they are compact and therefore easy to transport and store.
The tubes can be adjusted and fixed by means of screwed quick-release fasteners made of robust plastic.
The innermost tube has an outer diameter of Ø 23 mm and a wall thickness of 1.5 mm.
At the end there is a plastic attachment with a male thread size M20.

Available accessories: plastic end piece with M20 thread, angle connection with cutting thread, brush attachment with hose (suitable for angle connection with cutting thread)

Standard dimensions

max. length extended (m)

Length retracted

Number of tubes

Weight (g)Surface

3

1,67

2

533

3k / matt

4

1,52

3

785

3k / matt

5

1,85

3

970

3k / matt

6

1,74

4

1.260

3k / matt

7

1,99

4

1.440

3k / matt

8

1,9

5

1.780

3k / matt

9

1,83

6

2.000

3k / matt

10

2,05

6

2.42

3k / matt

11

2,22

6

2.620

3k / matt

12

1,93

8

3.120

3k / matt

13

2,15

8

3.730

3k / matt

14

1,17

8

3.950

3k / matt

15

2,39

8

4.210

3k / matt

16

2,46

8

4.420

3k / matt

17

2,58

8

4.660

3k / matt

18

2,71

8

4.910

3k / matt

The details of CFP profiles can vary depending on the type of fibre reinforcement, shape and wall thickness.

Carbon Profile Type pultrudedPullwindingPrePreg
 ZXZXZX
Tensile strength1.700 MPa80 MPa1.700 MPa80 MPa950 MPa900 MPa
Flexural strength1.700 MPa 1.600 MPa 1.050 MPa900 MPa
I.L.S.S interlaminar shear strength    68 MPa70 MPa
E-modulus (tensile strength)115 GPa 110 GPa 60 MPa60 MPa
E-modulus (bending)110 GPa 110 GPa 62 MPa60 MPa
Elongation at breakapprox. 0,5 % approx. 1 %   
Compressive strength450 MPa 450MPa   
Compressive modulus30 GPa 30GPa   
Density1,6 kg/dm³ 1,65 kg/dm³   
Compressive modulus of elasticity120 GPa 30 GPa   
Impact strength2.000 kJ/m² 30 kJ/m²   
Barcol Hardness45 45   
Characteristic value for all types 
interlaminar shear strength

90 MPa

Lin.coefficient of thermal expansion

0,1 x 10 -61/K

Thermal conductivity

5,2 W/mK

Water absorption

0,10%

Dimensional stability according to Martens

130°C

Carbon fibres

T300