PULTRUDIRANE OGLJIKOVE CEVI/PROGE

(postopek ekstrudiranja) so sestavljeni iz ogljikovih vlaken, ki so bila potegnjena skozi kopel smole in nato skozi segreto orodje.

Vzdolžne sile absorbirajo rovingi (enosmerna ogljikova vlakna), strižne sile pa matrica smole.

Standardne dimenzije

Zunanji premer (mm) x notranji premer (mm)

1.5 x 1.0

1.8 x 1.0

2.0 x 1.5

2.5 x 1.5

3.0 x 1.5

3.0 x 2.0

3.5 x 2.0

1.0 x 2.0

4.0 x 2.5

4.0 x 3.0

4.5 x 2.5

4.5 x 3.0

5.0 x 1.0

5.0 x 2.0

5.0 x 2.5

5.0 x 3.0

5.0 x 3.5

5.0 x 4.0

5.5 x 3.5

5.5 x 4.5

6.0 x 3.0

6.0 x 4.0

6.0 x 4.5

6.0 x 5.0

7.0 x 5.0

7.0 x 6.0

8.0 x 4.0

8.0 x 5.0

8.0 x 6.0

8.0 x 6.5

8.0 x 7.0

8.5 x 6.5

9.0 x 7.0

9.5 x 7.5

10.0 x 6.0

10.0 x 7.0

10.0 x 8.0

10.0 x 9.0

12.0 x 8.0

11.0 x 8.0

12.0 x 8.0

12.0 x 10.0

14.0 x 12.0

16.0 x 12.0

16.0 x 14.0

18.0 x 16.0

20.0 x 18.0

20.0 x 16.0

24.0 x 22.0

25.0 x 20.0

25.0 x 22.0

27.9 x 22.5

28.7 x 24.7

37.0 x 30.0

35.0 x 30.0

na zahtevo

 

Podatki o profilih CFP se lahko razlikujejo glede na vrsto vlakenske ojačitve, obliko in debelino stene.

Karbonovi profili tipa pultrudiraninavijanje z vlekoPrePreg
ZXZXZX
Natezna trdnost1.700 MPa80 MPa1.700 MPa80 MPa750 MPa700 MPa
Upogibna trdnost1.700 MPa1.600 MPa300 MPa300 MPa
I.L.S.S – medplastna strižna trdnost68 MPa70 MPa
Modul elastičnosti (togost)115 GPa110 GPa60 MPa60 MPa
Modul elastičnosti (upogib)110 GPa110 GPa62 MPa60 MPa
Raztezek pri prelomupribližno 0,5 %pribl. 1 %
Tlačna trdnost450 MPa450 MPa
Tlačni modul30 GPa30 GPa
Gostota1,6 kg/dm³1,65 kg/dm³
Tlak, modul elastičnosti120 GPa30 GPa
Udarna trdnost IZOD2.000 kJ/m²30 kJ/m²
Barcolova trdota4545
Karakteristična vrednost za vse tipe
medplastna strižna trdnost

90 MPa

Linearni koeficient toplotnega raztezanja

0,1 × 10⁻⁶¹/K

Toplotna prevodnost

5,2 W/mK

Vpijanje vode

0,10 %

Oblikovna stabilnost po Martensu

130 °C

Ogljikova vlakna

T300