Os testes foram realizados com perfis de PRFV. A inflamabilidade deve ser coordenada com a respectiva aplicação.


Padrão   Método de teste /
observação
País Resultado
ÖNORM B 3800   B1-Test/
phenolic resin
A B1 Tr1 Q1
UNIFER E 10.02.977   UNI 9177
classification
CH, I 2A
UNIFER E 10.02.977   UNI 9174
burning heat FT
CH, I 2A
UNIFER E 10.02.977   UNI 8457 KI FT CH, I 2A
UNIFER E 10.02.977   ISO 5660-1
heating energy
CH, I see test report
UNIFER E 10.02.977   EN ISO 1716
heating value
CH, I 7639 J/g
DIN 53 438, part 2   5 mm D K 1/5 mm
DIN 54837   DIN 55 10 T2 D S4 SR2 ST2
DIN EN 13501 –1   DIN EN
ISO 9239 -1
D EU 9,9 kW/m2 /
195% min
DIN EN 13501 –1   DIN EN
ISO 11925-2
D EU standards fulfilled
DIN EN 13501 –1   (≈DIN 4102-B1) D EU Bfl –s1
NFF16 -101   NF X 70 -100
toxicity
F F1/I.T.C.-Wert: 2,3
NFF16 -101   NF X 10 -702
smoke
F F1/I.T.C.-Wert: 2,3
NFF16 -101   NF P 92-501 fire F M 2
BS 476: Part 7: 1997   8 mm GB class 2
BS 476: Part 7: 1997   3 mm GB class 2
UIC 564-2: 1994   Annex 4 H fire C / smoke A
NFPA 130   ASTM E 662
smoke density
USA see test report
NFPA 130   ASTM E 162
flame spread
USA Is = 9,7
NFPA 255   ASTM E-84-98 USA < 25, class A
Code 95/28/EG: 1995   automobile code,
burning speed
95/28/EG: 1995
EU standards fulfilled
EN ISO 11925-2: 2002   CEN/TS
45545-2: 2009
ignition
EU standards fulfilled
ISO 5660-1: 2002   CEN/TS
45545-2: 2009
heat release
EU MAHRE 50,7 kW/m2
ISO 5658-2: 2006   CEN/TS
45545-2: 2009
flame spread
EU CFE > 20 kW/m2
Qsb 8,13 MJ/m2
ISO 5659-2: 2007   CEN/TS
45545-2: 2009
smoke toxicity
EU Ds (4) 89
VOF 4 95
CIT 4 min 0,01
CIT 8 min 0,02
ISO 4589-2   oxygen index
by RT
EU LOI 36,2%
DIN EN 60695-11-10   vertical test
UL94 V
EU V 0
EN 45545   EN 45545-2:2013 EU HL 1-3
EN ISO 5659-2:2012   EN 45545-2:2013 EU 25bW/m², Ds max 109
NF X 70-100-1:2006   EN 45545-2:2013 EU T12, CITNLP 0,03
DIN EN ISO 4589-2:2006   EN 45545-2:2013 EU LOI 36%
DIN EN 13823:2010   DIN EN 13501-1:2010 EU B, s1, d0